Influence of Annealing Temperature on Electrical Properties of Unmodified Bentonite



Abstract Views
232

Downloads
248

Citations

Share

##plugins.themes.bootstrap3.article.sidebar##

Submitted Feb 26, 2018
Published Jun 27, 2018
10.24018/ejeng.2018.3.6.624

Abstract viewed = 232 times

Table of Contents

##plugins.themes.bootstrap3.article.main##

In this work, influence of annealing temperature on the electrical properties of unmodified bentonite has been investigated. It is concluded that, by the increase of annealing temperature, the values of permittivity and conductivity are decreased, but the electric resistance and the density of the bentonite are increased. It is also shown that the basic reason for this is the presence of water molecules and alkaline oxides such as Na2O, K2O in bentonite.

Keywords: Polymer Bentonite Composite Montmorillonite Nanocomposite Conductivity Resistivity

Downloads

Download data is not yet available.

References

  1. Л.Бесланеева, М.Х. Лигидов, А.К. Микитаев, Ю.И. Мусаев, С.И.Пахомов, С.Ю.Хаширова "Разработка новых органоглин, для получения полимерных нанокомпозитов с регулируемыми свойствами " Известия вузов. Химия и химическая технология. – 2011. – Т. 54. № 5. – С. 86-88.
     Google Scholar
  2. S. Wang, Y. Hu, L. Song, Z. Wang, Z. Chen, W. Fan. "Preparation and thermal properties of ABS/montmorillonite nanocomposite "Polym.Degrad. Stab. – 2002. – V. 77. – P. 423-426.
     Google Scholar
  3. J.C. Huang, Z.K. Zhu, X.D. Ma, X.F. Qian, J. Yin." Preparation and properties of montmorillonite/organosoluble polyimide hybrid materials prepared by a one-step appro ". Journal of Materials Science. – 2001. – V. 36. – Р. 871–877.
     Google Scholar
  4. Gilman, J.W. Nanocomposites:" A revolutionary new flame retardant approach ". SAMPE J. – 1997. – V. 33. – P. 40–46.
     Google Scholar
  5. Михайлин Ю.А. "Термоустойчивые полимеры и полимерные материалы ".СПб.: Профессия, 2006. – 623 с.
     Google Scholar
  6. J. J. Tunney, C. Detelliera. “luminosilicate nanocomposite materials. poly (ethylene glycol)-kaolinite intercalates " Chem. Mater. – 1996. – V.8. – P. 927-935.
     Google Scholar
  7. Ш.М.Гасанли, С.Р.Иманова, "Электрофизические характеристики композитных нелинейных резисторов на основе полимера и бентонита "Электронная обработка материалов, 2017, 53(4), p. 85–89.
     Google Scholar
  8. Першин Е.Д., Карпушин Н.А., Каздобин К.А. "Проводимость алюмосиликатов в присутствии воды. Электронная обработка материалов "2010, №4, с-60-67.
     Google Scholar
  9. Хаширова С.Ю., Бесланеева З.Л., Мусов И.В., Мусаев Ю.И., Микитаев А.К. "Cпектральное исследование взаимодействия акрилата и метакрилата гуанидина с монтмориллонитом " Фундаментальные исследования. – 2011. – № 8-1. – С. 202-206;
     Google Scholar
  10. Т.Л.Ракитская1,Т.А.Киоселев,А.М.Джига."ИК-спектральное исследование структуры бентонита".Вестник Одеского Политехнического Университета. Химия том 17 выпуск 1(42) 2012 стр.13-19.
     Google Scholar